910 ALLOY
$38.00
910 ALLOY is a measurable advancement in 3D Printing materials technology from Taulman 3D.
Flex Resistant Glass is required when using this material:
Flex Resistant Glass for AXIOM series.
910 Alloy is the combined effort of chemical companies, extrusion manufactures and Taulman 3D to specifically develop a single material to meet as many high performance 3D Printing needs as possible. With a combined tensile strength higher than the strongest co-polyesters, the durability of Nylons, a shrinkage factor that rivals our t-glase, a vast range of chemical resistance and a 95C working range, you now have one solution easily printable at 245C.
NOTE: 910 Alloy is the only Nylon-based polymer that makes support removal easier than most.
Specifications:
Tensile Strength = 8,100PSI +
Modulus PSI = 72,932
Max Elongation at break = 31%
Print Temperature = 245C
Nozzle size = Any – There are no particulates or additives in Alloy 910
Tg = 90C
Print Bed = 80
Hot = Glass heated to 80C with coat of PVA
(PVA is 50% water and 50% “Elmers Glue All”)
Shrinkage = 0.0031 in/in
Transmission = 50%
Color = Natural
| Shipping Weight | 1.1 lbs |
|---|---|
| Shipping Dimensions | 8 × 8 × 3 in |
| Color | Black 2.2lbs, Natural 2.2lbs |
| Extruder Temperature | 240C – 250C |
| Bed Temperature | 70C – 80C |
| Heated Bed | No |
| Recommended Build Surface | Wolfbite NITRO |
| Diameter | 2.88mm |
| Compatible Machine | AXIOM, AXIOM 20, AXIOM Dual Extruder, EVO |
| Tensile Strength | 47.7 MPa |
| Elongation at Break | 28.8% |
| Typical Application | Prosthetics |
| Specifications | |
| Tensile Strength | 47.7 MPa |
|---|---|
| Elongation at Break | 28.8% |
| Extruder Temperature | 240C - 250C |
| Bed Temperature | 70C - 80C |
| Heated Bed | No |
| Recommended Build Surface | Wolfbite NITRO |
| Diameter | 2.88mm |
| Color | Black 2.2lbs, Natural 2.2lbs |
| Compatible Machine | AXIOM, AXIOM 20, AXIOM Dual Extruder, EVO |
| Applications | |